Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.68 g/cc
0.0607 lb/in³
ISO 1183
Filler Content填料含量
30 %
Mechanical Properties力学性能
Tensile Strength at Break断裂拉伸强度
133 MPa
@Temperature 23.0 °C
19300 psi
@Temperature 73.4 °F
ISO 527
Elongation at Break断裂伸长率
1.9 %
@Temperature 23.0 °C
1.9 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus拉伸模量
11.3 GPa
@Temperature 23.0 °C
1640 ksi
@Temperature 73.4 °F
Flexural Modulus弯曲弹性模量
10.5 GPa
@Temperature 23.0 °C
1520 ksi
@Temperature 73.4 °F
ISO 178
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)
8.50 kJ/m²
@Temperature 23.0 °C
4.04 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)
40.0 kJ/m²
@Temperature 23.0 °C
19.0 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击
4.00 J/cm²
@Temperature 23.0 °C
19.0 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击
0.900 J/cm²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Electrical Properties电性能
Comparative Tracking Index漏电起痕指数
200 V
@Temperature 23.0 °C
200 V
@Temperature 73.4 °F
IEC 60112
250 - 400 V
@Temperature 23.0 °C
250 - 400 V
@Temperature 73.4 °F
UL 746A
Thermal Properties热性能
UL RTI, Electrical相对温度指数
155 °C
@Thickness 3.00 mm
311 °F
@Thickness 0.118 in
UL 746B
155 °C
@Thickness 0.350 mm
311 °F
@Thickness 0.0138 in
UL RTI, Mechanical with Impact机械冲击热指数
155 °C
@Thickness 1.50 mm
311 °F
@Thickness 0.0591 in
UL 746B
155 °C
@Thickness 2.00 mm
311 °F
@Thickness 0.0787 in
UL RTI, Mechanical without Impact无机械冲击热指数
155 °C
@Thickness 2.00 mm
311 °F
@Thickness 0.0787 in
Flammability, UL94阻燃等级
V-0
@Thickness 2.00 mm
V-0
@Thickness 0.0787 in
IEC 60695-11-10
5VA
@Thickness 1.50 mm
5VA
@Thickness 0.0591 in
UL94
Glow Wire Test灼热丝试验
800 °C
@Thickness 0.750 mm
1470 °F
@Thickness 0.0295 in
Ignition; IEC 60695-2-13
985 °C
@Thickness 3.00 mm
1810 °F
@Thickness 0.118 in
Processing Properties加工性能
Melt Temperature熔体温度
252 °C
486 °F
10°C/min; ISO 11357-1/-3
270 - 290 °C
518 - 554 °F
Mold Temperature模具温度
90.0 - 110 °C
194 - 230 °F
110 °C
230 °F
optimum
Drying Temperature干燥温度
120 °C
248 °F
Dry Time干燥时间
4.00 hour
Moisture Content水分含量
<= 0.020 %
FR530L BK507是美国杜邦公司聚对苯二甲酸乙二醇酯（polyethylene terephthalate）PET型号之一,商品名Rynite,是一种高度结晶性聚合物,表面平滑高光泽,高透明度,低吸水性,耐水解,具有优良的力学特性,高刚性,高耐力,耐折性好,耐稀酸,稀碱,耐脂肪,耐油性,耐大多数溶剂,（增强级）耐高温（+150℃）低温（-70℃）,耐热老化,电绝缘性佳,低渗透率,高阻隔性,无毒无味,抗蠕变,耐疲劳,耐摩擦,尺寸稳定,可以用传统的成型方法加工,广泛用于卫浴用品,化妆品,电子电器,机械器材,复杂薄壁产品等。中国塑商之家塑料网为您提供 PET FR530L BK507的物性参数,加工参数,PET UL黄卡,PET SGS报告,PET RoHS报告,PET Reach报告,PET SDS MSDS报告,PET FDA报告,PET PFOS报告,PET PFOA报告,PET SVHC报告,PET塑料价格,PET塑料批发信息,PET塑料供应信息